Effect of Hydrogen Plasma on Model Corrosion Layers of Bronze

Loading...
Thumbnail Image
Date
2016-05-17
ORCID
Advisor
Referee
Mark
Journal Title
Journal ISSN
Volume Title
Publisher
IOP Publishing
Altmetrics
Abstract
Our work is about plasmachemical reduction of model corrosion layers. The model corrosion layers were produced on bronze samples with size of 10 x 10 x 5 mm3, containing Cu and Sn. Concentrated hydrochloric acid was used as a corrosive environment. The application of reduction process in low-pressure low-temperature hydrogen plasma followed. A quartz cylindrical reactor with two outer copper electrodes was used. Plasma discharge was generated in pure hydrogen by a RF generator. Each corroded sample was treated in different conditions (supplied power and a continual or pulsed regime with a variable duty cycle mode). Process monitoring was ensured by optical emission spectroscopy. After treatment, samples were analyzed by SEM and EDX.
Práce je zaměřena na plazmochemickou redukci modelových korozních vrstev. Modelové korozní vrstvy byly připraveny na bronzových vzorcích o rozměrech 10 x 10 x 5 mm3. Jako korozní prostředí byly použity páry koncentrované kyseliny chlorovodíkové. Pro redukci byl použit křemenný válcový reaktor s vnějšími měděnými elektrodami, RF výboj byl generován v čistém vodíku. Každý korodovaný vzorek byl v plazmatu ošetřen za odlišných podmínek (výkon, střída), proces byl monitorován optickou emisní spektrometrií. Po opracování byly vzorky analyzovány pomocí SEM a EDX.
Description
Citation
Journal of Physics: Conference Series. 2016, vol. 715, issue 1, p. 012006-1-012006-4.
http://iopscience.iop.org/article/10.1088/1742-6596/715/1/012006/
Document type
Peer-reviewed
Document version
Published version
Date of access to the full text
Language of document
en
Study field
Comittee
Date of acceptance
Defence
Result of defence
Document licence
Creative Commons Attribution 3.0 Unported
http://creativecommons.org/licenses/by/3.0/
Citace PRO