Aerosol Flow Homogenization in the Spray Polyphenylene Vinylene Thin Film Deposition

Abstract

Two different spray deposition (SD) techniques were compared on polyvinylene (MDMO-PPV) used as a model material. SD and homogenized (h-SD) techniques were compared. Films of about 1 micron thickness were prepared by SD and h-SD and normal techniques from toluene solution with a concentration of 0.5 g/l. It was found that the ITO|MDMO-PPV|Al structures with h-SD MDMO-PPV films behave as a photovoltaic cell. Optical micrograph images show structure with typical discs. Current - voltage characteristics measured on samples with h-SD films show that an exposure to a white light increases the current two orders of magnitude.

Dvě různé techniky sprajové depozice (SD) byly porovnány na polyvinylenu (MDMO-PPV) použité jako modelové materiály. Techniky SD a sprayové depozice z homogenizovaného aerosolu (h-SD) byly porovnány. Filmy o tloušťce přibližně 1 mikrometru byly připraveny metodami SD a h-SD a normálními technikami z roztoku v toluenu o koncentraci 0.5 g/l. Bylo zjištěno, že struktura ITO|MDMO-PPV|Al připravená metodou h-SD se chová jako fotovoltaický článek. Na fotografiích z mikroskopu vzorky vykazovaly typickou diskovou strukturu. Na voltampérových charakteristikách se projevilo zvýšení proudu o dva řády při ozáření bílým světlem.