Abstract

High compressive strength heavyweight concrete specimens were prepared using two types of high-density aggregates, Portland cement, and SCMs. Elemental composition of aggregates and cementitious materials were performed by NAA, PGAA, and XRF methods. The mechanical and physical properties confirm that these concretes meet the requirements of concrete strength grade C55/67 after 28 days of curing, which makes them considered High Compressive Strength Concretes. The fresh and dry density values far exceed 3,000 kg m-3. Other properties, tensile strength and modulus of elasticity provide basic evidence to support the idea that these concretes could be considered as High-Performance Heavyweight concretes. Also, the ingredients of the above concrete showed good activation properties.

Na základe predošlých výskumov v oblasti ťažkých betónov boli pripravené vzorky za použitia dvoch ťažkých kamenív s vysokou objemovou hmotnosťou, portlandského cementu a SCMs. Analýza chemického zloženia plniva aj spojiva bola realizovaná pomocou troch metód a to NAA, PGAA a XRF. Z výsledkov fyzikálno-mechanických vlastností vzoriek je zrejmé, že vzorky po 28 dňoch dosiahli triedu pevnosti betónu C55/67. Hodnoty objemovej hmotnosti betónu sa zisťovali v čerstvom aj v zatvrdnutom stave a značne presahujú 3000 kg m-3. Ostatné sledované vlastnosti preukazujú, že tieto betóny je možné oznať za vysokopevnostné ťažké betóny. Rovnako použité materiály preukázali dobré aktivačné vlastnosti.