dc.contributor.authorMikhailova, Olesiacs
dc.contributor.authorRovnaník, Pavelcs
dc.date.accessioned2022-05-10T14:54:12Z
dc.date.available2022-05-10T14:54:12Z
dc.date.issued2016-06-01cs
dc.identifier.citationProcedia Engineering. 2016, vol. 151, issue 1, p. 222-228.en
dc.identifier.issn1877-7058cs
dc.identifier.other131371cs
dc.identifier.urihttp://hdl.handle.net/11012/204206
dc.description.abstractPolyethylene glycol is a non-toxic water soluble polymer often used in many industrial applications. The aim of this paper is to study the effect of polyethylene glycol with relative molecular weight ranging between 400–20000 on the properties of geopolymer mortars composed of metakaolin and sodium silicate. Polyethylene glycol was added in the amount of 0.5 to 10% by mass of metakaolin. After 28 days of curing at ambient conditions, different tests were carried out: physico-chemical (density, porosity), mechanical (flexural and compressive strength) and structural (SEM). The results showed that a maximum compressive strength of 23.9 MPa and a maximum flexural strength of 2.9 MPa were achieved by adding 10% PEG 400.reference values with higher amount of MWCNTs.en
dc.description.abstractPolyethylenglykol je zdravotně nezávadný vodou rozpustný polymer, často používaný v mnoha průmyslových aplikacích. Cílem této práce je studovat vliv polyethylenglykolu s relativní molekulovou hmotností v rozmezí 400 – 20000 na vlastnosti geopolymerní malty složené z metakaolinu a křemičitanu sodného. Polyethylenglykol byl přidán v množství 0,5 až 10 % z hmotnosti metakaolinu. Po 28 dnech zrání byly provedeny různé testy: fyzikálně chemické (hustota, porozita), mechanické (pevnost v ohybu a v tlaku) a mikrostrukturní (SEM). Výsledky ukázaly, že maximální pevnosti v tlaku 23,9 MPa a maximální pevnosti v tahu za ohybu 2,9 MPa bylo dosaženo přidáním 10 % PEG 400.cs
dc.formattextcs
dc.format.extent222-228cs
dc.format.mimetypeapplication/pdfcs
dc.language.isoencs
dc.publisherElseviercs
dc.relation.ispartofProcedia Engineeringcs
dc.relation.urihttps://www.sciencedirect.com/science/article/pii/S1877705816317672cs
dc.rightsCreative Commons Attribution-NonCommercial-NoDerivatives 4.0 Internationalcs
dc.rights.urihttp://creativecommons.org/licenses/by-nc-nd/4.0/cs
dc.subjectMetakaolinen
dc.subjectgeopolymeren
dc.subjectpolyethylene glycolen
dc.subjectmechanical propertiesen
dc.subjectmicrostructureen
dc.subjectMetakaolin
dc.subjectgeopolymer
dc.subjectpolyethylenglykol
dc.subjectmechanické vlastnosti
dc.subjectmikrostruktura
dc.titleEffect of polyethylene glycol addition on metakaolin-based geopolymeren
dc.title.alternativeVliv přídavku polyethylenglykolu na vlastnosti metakaolinového geopolymerucs
thesis.grantorVysoké učení technické v Brně. Fakulta stavební. Ústav chemiecs
thesis.grantorVysoké učení technické v Brně. Fakulta stavební. AdMaS Divize TSHcs
sync.item.dbidVAV-131371en
sync.item.dbtypeVAVen
sync.item.insts2022.05.10 16:54:12en
sync.item.modts2022.05.10 16:14:12en
dc.coverage.issue1cs
dc.coverage.volume151cs
dc.identifier.doi10.1016/j.proeng.2016.07.379cs
dc.rights.accessopenAccesscs
dc.rights.sherpahttp://www.sherpa.ac.uk/romeo/issn/1877-7058/cs
dc.type.driverconferenceObjecten
dc.type.statusPeer-revieweden
dc.type.versionpublishedVersionen


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record

Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International
Except where otherwise noted, this item's license is described as Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International