• čeština
    • English
    • русский
    • Deutsch
    • français
    • polski
    • українська
  • English 
    • čeština
    • English
    • русский
    • Deutsch
    • français
    • polski
    • українська
  • Login
View Item 
  •   Repository Home
  • Závěrečné práce
  • dizertační práce
  • Fakulta strojního inženýrství
  • 2010
  • View Item
  •   Repository Home
  • Závěrečné práce
  • dizertační práce
  • Fakulta strojního inženýrství
  • 2010
  • View Item
JavaScript is disabled for your browser. Some features of this site may not work without it.

Vliv plasmové nitridace na únavovou životnost vysocepevných ocelí při biaxiálním zatěžování

Influence of Plasma-nitriding on Fatigue Life of High-strength Steels under Biaxial Loading

Thumbnail
View/Open
final-thesis.pdf (6.967Mb)
thesis-1.pdf (1.979Mb)
review_33017.html (1.916Kb)
Author
Major, Štěpán
Advisor
Pokluda, Jaroslav
Referee
Kohout, Jan
Růžička,, Milan
Obrtlík, Karel
Grade
P
Altmetrics
Metadata
Show full item record
Abstract
Tato práce se věnuje únavové životnosti vzorků, vyrobených z vysocepevné oceli s nitridovanou vrstvou a bez ní. Vzorky byly podrobeny soufázové kombinaci ohybu a krutu. Práce je zaměřena na tři druhy problémů. Za prvé byl studován vztah mezi únavovou životností a přítomností povrchové vrstvy. V této práci bylo jednoznačně prokázáno, že přítomnost povrchové vrstvy má pozitivní vliv na únavovou životnost v oblasti vysokocyklové únavy. Zároveň byla analyzována jednotlivá únavová kritéria a posuzována jejich efektivita. Nejlepší kritéria jsou Marinovo a Matakovo.Druhým cílem této práce bylo posouzení vztahu mezi součinitelem namáhání ( je amplituda ohybového namáhání a amplituda namáhání v krutu) a topografií lomového povrchu v oblasti vysokocyklové únavy. Vlastnosti lomového povrchu byly kvantifikovány pomocí množství parametrů drsnosti. Mnoho parametrů drsnosti prudce roste nad kritickou hodnotou se součinitelem namáhání zc = 0,5. Posledním cílem této práce byla fraktografická analýza trhlin typu rybí oko, které byly generovány v nitridovaných vzorcích.
 
This work deals with fatigue life and fractographycal analysis of plasma-nitrided and virgin specimen made of the low-alloy high-strength steel. Specimens were subjected to in-phase combined bending-torsion loading. The work is focused on three groups of problems. The first group of problems was associated with the fatigue life and its prediction. The objective was to examine a relationship between the presence of the nitrided layer and fatigue life. The application of surface layers has significantly improved the fatigue life in the high-cycle region. An extended comparison between classical and advanced multiaxial criteria was performed. Criterions proposed by Marin and Matake were found to be most precise. The second objective of this work was to examine a relationship between the loading ratio ( is the bending amplitude and is the torsion amplitude ) and the fracture surface topography in the highcycle fatigue. Properties of fracture surfaces were quantified by many roughness and fractal parameters. Many roughness parameters start to incrise rapidly above a critical value of the loading ratio zc = 0,5. The last part of this work deals with the fractographical analysis of fish-eye cracks that were formed in plasma-nitrided steel specimens under symetrical bending, symetrical torsion and biaxial in-phase bending-torsion combinations.
 
Keywords
biaxiální namáhání, únava, fraktografie, rybí oko, Biaxial Loading, Fatigue, Fractography, Fish-eye crack.
Language
čeština (Czech)
Study brunch
Fyzikální a materiálové inženýrství
Composition of Committee
prof. Ing. Jiří Švejcar, CSc. (předseda) prof. RNDr. Jan Kohout, CSc. (člen) prof. Ing. Milan Růžička, CSc. (člen) doc. RNDr. Karel Obrtlík, CSc. (člen) prof. RNDr. Miroslav Liška, DrSc. (člen) prof. RNDr. Zdeněk Knésl, CSc. (člen)
Date of defence
2010-06-22
Process of defence
Z posudků oponentů i z diskuse vyplynulo, že DP přinesla nové poznatky tím, že doktorand v ní vysvětlil pozitivní vliv nitridované vrstvy na víceosou únavovou životnost vysocepevné oceli a popsal geometrii a způsob šíření trhlin typu "rybí oko" při kombinovaném krutu a ohybu. V diskusi bylo také uvedeno, že i když některé výsledky práce byly již publikovány v časopisech, mnohé další by bylo vhodné ještě zveřejnit.
Result of the defence
práce byla úspěšně obhájena
Persistent identifier
http://hdl.handle.net/11012/4400
Source
MAJOR, Š. Vliv plasmové nitridace na únavovou životnost vysocepevných ocelí při biaxiálním zatěžování [online]. Brno: Vysoké učení technické v Brně. Fakulta strojního inženýrství. 2010.
Collections
  • 2010 [55]
Citace PRO

Portal of libraries | Central library on Facebook
DSpace software copyright © 2002-2015  DuraSpace
Contact Us | Send Feedback | Theme by @mire NV
 

 

Browse

All of repositoryCommunities & CollectionsBy Issue DateAuthorsTitlesSubjectsThis CollectionBy Issue DateAuthorsTitlesSubjects

My Account

LoginRegister

Statistics

View Usage Statistics

Portal of libraries | Central library on Facebook
DSpace software copyright © 2002-2015  DuraSpace
Contact Us | Send Feedback | Theme by @mire NV