Mechanical properties of a biodegradable self-expandable polydioxanone monofilament stent: In vitro force relaxation and its clinical relevance

Biodegradable stents are promising treatments for many diseases, e.g., coronary artery disease, urethral diseases, tracheal diseases, and esophageal strictures. The mechanical properties of biodegradable stent materials play a key role in the safety and efficacy of treatment. In particular, insufficient creep resistance of the stent material could result in premature stent collapse or narrowing. Commercially available biodegradable self-expandable SX-ELLA stents made of polydioxanone monofilament were tested. A new, simple, and affordable method to measure the shear modulus of tiny viscoelastic wires is presented. The important mechanical parameters of the polydioxanone filament were obtained: the median Young's modulus was (E) over tilde = 958 (922, 974) MPa and the shear modulus was (G) over tilde= 357 (185, 387) MPa, resulting in a Poisson's ratio of nu = 0.34. The SX-ELLA stents exhibited significant force relaxation due to the stress relaxation of the polydioxanone monofilament, approximately 19% and 36% 10 min and 48 h after stent application, respectively. However, these results were expected, and the manufacturer and implanting clinician should be aware of the known behavior of these biodegradable materials. If possible, a biodegradable stent should be designed considering therapeutic force rather than initial force. Additionally, new and more advanced biodegradable shape-memory polymers should be considered for future study and use.

Keywords

BENIGN ESOPHAGEAL STRICTURES, SUTURE MATERIALS, MEMORY, DEGRADATION, COMPOSITES, STRENGTH, BEHAVIOR, FIBERS, MODELS, CREEP

Citation

PLOS ONE. 2020, vol. 15, issue 7, p. 1-16.
https://journals.plos.org/plosone/article?id=10.1371/journal.pone.0235842

Document type

Peer-reviewed

Document version

Published version

Language of document

en

Document licence

Creative Commons Attribution 4.0 International
http://creativecommons.org/licenses/by/4.0/