Non-aqueous template-assisted synthesis of mesoporous nanocrystalline silicon orthophosphate

The first synthesis of mesoporous nanocrystalline silicon orthophosphate Si5P6O25 is presented. The synthetic procedure is based on the non-hydrolytic sol-gel reaction in the presence of Pluronic P123 template and subsequent calcination in air. The condensation of silicon acetate, Si(OAc)(4), and tris(trimethylsilyl) phosphate, OP(OSiMe3)(3) (TTP), in non-aqueous solvents driven by elimination of trimethylsilyl acetate provides a homogeneous network with a high content of Si-O-P bonds and SiO6 moieties. After burning out the template, mesoporous silicon orthophosphate was obtained with surface areas up to 128 m(2) g(-1) and pore sizes around 20 nm. The nanocrystalline Si5P6O25 phase forms relatively easily (500 degrees C, 4 h) in comparison with other synthetic routes. All samples were characterized by SEM, TEM, elemental analysis, TGA, nitrogen adsorption, SAXS, H-1, C-13, Si-29, and P-31 solid-state NMR spectroscopy, and powder XRD. These xerogels showed superior catalytic activity and selectivity in methylstyrene dimerization.

Keywords

phosphoric-acid catalyst, organic-inorganic hybrid, sol-gel synthesis, phosphosilicate gels, ambient conditions, crystal-structure, molecular-sieves, surface-area, MAS NMR, glasses

Citation

RSC Advances. 2015, vol. 5, issue 90, p. 73670-73676.
https://pubs.rsc.org/en/content/articlehtml/2015/ra/c5ra10982e

Document type

Peer-reviewed

Document version

Published version

Language of document

en